- 弯曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 165 MPa | 23900 psi | |||
| Elongation at Yield | 2.5 % | 2.5 % | |||
| 3.2 % | 3.2 % | flexural | |||
| Modulus of Elasticity | 23.0 GPa | 3340 ksi | |||
| Flexural Strength | 235 MPa | 34100 psi | |||
| Flexural Modulus | 20.0 GPa | 2900 ksi | |||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | flatwise; ISO 179 1fU | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 100 ohm | <= 100 ohm | |||
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | DIN 53752 | ||
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| 140 °C | 284 °F | short term | |||
| Vicat Softening Point | 170 °C | 338 °F | DIN ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 250 °C | 482 °F | mass temp | ||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |||
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |||
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |||
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |||
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec | 167 °F @Time 6.00 - 10.0 hour | Dehumidifying dryer | ||
| 105 °C @Time <=14400 sec | 221 °F @Time <=4.00 hour | or | |||
| Descriptive Properties | |||||
| Color | natural color (black) | ||||