- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 1.30
- 硬度: 100.0
- 热变形温度 [℃]: 127.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
Water Absorption | 0.20 % | 0.20 % | 24 hrs; ASTM D570 |
Water Absorption at Saturation | 1.4 % | 1.4 % | ASTM D570 |
Mechanical Properties | Metric | English | Comments |
Hardness, Rockwell R | 100 | 100 | ASTM D785 |
Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
Elongation at Break | 225 % | 225 % | ASTM D638 |
Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
0.240 J/cm @Temperature -40.0 °C | 0.450 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
Thermal Properties | Metric | English | Comments |
Melting Point | 184 °C | 363 °F | ASTM D3418 |
Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | ASTM D648 |