- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 47.6
- 弯曲模量 [MPa]: 1.86
- 热变形温度 [℃]: 128.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.016 - 0.017 cm/cm | 0.016 - 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 33.1 MPa | 4800 psi | ASTM D638 |
| Tensile Strength, Yield | 47.6 MPa | 6900 psi | ASTM D638 |
| Tensile Modulus | 1.93 GPa | 280 ksi | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9010 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.18 mm | 0.800 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 11.1 J/cm @Thickness 3.18 mm | 20.8 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.60 kJ/m² | 2.66 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 78.4 kJ/m² | 37.3 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 11.0 J | 8.11 ft-lb | ASTM D3763 |
| Impact Test | 21.3 J | 15.7 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D4496 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 94.0 µm/m-°C @Temperature 20.0 °C | 52.2 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 °C | 399 °F | |
| Mold Temperature | 82.2 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |