Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned)

Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned) 物性表: Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned)物性表及特性介绍,Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned)注塑参数详情,如需Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 17.7
  • 密度 [g/cm3]: 3.8
  • 弯曲强度 [MPa]: 34.0
  • 热变形温度 [℃]: 170.0
 
Physical PropertiesMetricEnglishComments
Density 3.80 g/cc0.137 lb/in³
Melt Flow 17.7 g/10 min
@Load 5.00 kg,
Temperature 235 °C
17.7 g/10 min
@Load 11.0 lb,
Temperature 455 °F
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 34.0 MPa4930 psi5 mm/min
Elongation at Break 4.0 %4.0 %5 mm/min
Tensile Modulus 4.60 GPa667 ksi1 mm/min
Charpy Impact Unnotched 1.69 J/cm²8.04 ft-lb/in²
 1.96 J/cm²
@Temperature -30.0 °C
9.33 ft-lb/in²
@Temperature -22.0 °F
Charpy Impact, Notched 0.390 J/cm²1.86 ft-lb/in²
 0.380 J/cm²
@Temperature -30.0 °C
1.81 ft-lb/in²
@Temperature -22.0 °F
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 10000 ohm-cm10000 ohm-cm
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 70.0 µm/m-°C
@Temperature 20.0 °C
38.9 µin/in-°F
@Temperature 68.0 °F
Melting Point 183 °C361 °F(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 170 °C338 °F
Deflection Temperature at 1.8 MPa (264 psi) 100 °C212 °F
Vicat Softening Point 170 °C338 °F50°C/hr; 50N
Flammability, UL94  HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
 HB
@Thickness 3.10 mm
HB
@Thickness 0.122 in

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47340.html

免责声明: 本文 Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4