- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 2.7
- 拉伸强度 [MPa]: 62.0
- 热变形温度 [℃]: 64.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 2.7 % | 2.7 % | |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min |
| Tensile Modulus | 1.66 GPa | 241 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.05 J/cm² @Temperature -30.0 °C | 5.00 ft-lb/in² @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
| Vicat Softening Point | 67.0 °C | 153 °F | 50°C/hr; 50N |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |