- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.95
- 拉伸强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 1.13
- 热变形温度 [℃]: 145.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec | 0.95 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.75 % @Temperature 20.0 °C | 0.75 % @Temperature 68.0 °F | 50% RH; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 71 | 71 | After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868 | ||
| 76 | 76 | Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868 | |||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Elongation at Break | <= 200 % | <= 200 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Elongation at Yield | 6.0 % | 6.0 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Flexural Modulus | 1.13 GPa | 164 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 186 °C | 367 °F | ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 250 °C | 482 °F | Recommended Extrusion Temperature | ||
| 230 - 280 °C | 446 - 536 °F | Extrusion Temperature Range | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Descriptive Properties | |||||
| Bio Based Carbon | 100% | ASTM 6866, Calculation | |||