- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.69
- 拉伸强度 [MPa]: 76.0
- 断裂伸长率 [%]: 98.0
- 弯曲模量 [MPa]: 5.51
- 热变形温度 [℃]: 182.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0047 cm/cm | 0.0047 in/in | SABIC Method |
| 0.0047 cm/cm @Time 86400 sec | 0.0047 in/in @Time 24.0 hour | ISO 294 | |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec | 0.0040 - 0.0060 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0093 cm/cm | 0.0093 in/in | SABIC Method |
| 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D955 | |
| 0.0093 cm/cm @Time 86400 sec | 0.0093 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ISO 527 |
| 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 | |
| 152 MPa | 22000 psi | ASTM D638 | |
| 153 MPa | 22200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | ISO 527 |
| 76.0 MPa | 11000 psi | 5 mm/min; ISO 527 | |
| 152 MPa | 22000 psi | ASTM D638 | |
| 153 MPa | 22200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| 2.7 % | 2.7 % | ASTM D638 | |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.2 % | 2.2 % | ISO 527 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| 2.7 % | 2.7 % | ASTM D638 | |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.83 GPa | 991 ksi | 1 mm/min; ISO 527 |
| 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| 352 MPa | 51100 psi | ISO 178 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 352 MPa | 51100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 5.52 GPa | 801 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 18.2 GPa | 2640 ksi | ISO 178 | |
| 18.2 GPa | 2640 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.45 | 0.45 | ASTM D3702 Modified |
| K (wear) Factor | 117 x 10-8 mm³/N-M | 58.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 91.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 51.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 92.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 51.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 92.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 51.1 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 19.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 19.4 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 19.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 182 °C | 360 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 182 °C @Thickness 3.20 mm | 360 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 171 °C @Thickness 3.20 mm | 340 °F @Thickness 0.126 in | unannealed; ASTM D648 | |