- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 5.5
- 拉伸强度 [MPa]: 82.0
- 断裂伸长率 [%]: 80.0
- 弯曲强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 2.70
- 热变形温度 [℃]: 85.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.48 g/cc | 0.0390 - 0.0535 lb/in³ | Average value: 1.28 g/cc Grade Count:12 |
| Water Absorption | 5.50 - 8.00 % | 5.50 - 8.00 % | Average value: 7.17 % Grade Count:6 |
| Moisture Absorption at Equilibrium | 1.50 - 2.10 % | 1.50 - 2.10 % | Average value: 1.90 % Grade Count:6 |
| Viscosity Test | 115 - 160 cm³/g | 115 - 160 cm³/g | Average value: 131 cm³/g Grade Count:6 |
| Linear Mold Shrinkage | 0.00400 cm/cm | 0.00400 in/in | Average value: 0.00400 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00900 cm/cm | 0.00900 in/in | Average value: 0.00900 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 84.0 - 90.0 | 84.0 - 90.0 | Average value: 86.5 Grade Count:6 |
| Ball Indentation Hardness | 130 - 262 MPa | 18900 - 38000 psi | Average value: 167 MPa Grade Count:6 |
| Tensile Strength, Ultimate | 120 - 220 MPa | 17400 - 31900 psi | Average value: 169 MPa Grade Count:7 |
| Tensile Strength, Yield | 82.0 - 90.0 MPa | 11900 - 13100 psi | Average value: 88.0 MPa Grade Count:5 |
| Elongation at Break | 3.00 - 50.0 % | 3.00 - 50.0 % | Average value: 21.7 % Grade Count:12 |
| Elongation at Yield | 6.00 - 9.00 % | 6.00 - 9.00 % | Average value: 8.10 % Grade Count:5 |
| Modulus of Elasticity | 2.20 - 11.0 GPa | 319 - 1600 ksi | Average value: 6.48 GPa Grade Count:12 |
| Flexural Yield Strength | 80.0 - 342 MPa | 11600 - 49600 psi | Average value: 153 MPa Grade Count:6 |
| Flexural Modulus | 2.70 - 12.0 GPa | 392 - 1740 ksi | Average value: 4.45 GPa Grade Count:6 |
| Izod Impact, Unnotched (ISO) | 9.50 - 9.50 kJ/m² @Temperature -40.0 - -40.0 °C | 4.52 - 4.52 ft-lb/in² @Temperature -40.0 - -40.0 °F | Average value: 9.50 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 8.00 J/cm² - NB | 38.1 ft-lb/in² - NB | Average value: 9.37 J/cm² Grade Count:12 |
| 7.00 J/cm² - NB @Temperature -30.0 - 0.000 °C | 33.3 ft-lb/in² - NB @Temperature -22.0 - 32.0 °F | Average value: 7.46 J/cm² Grade Count:12 | |
| Charpy Impact, Notched | 0.900 - 2.10 J/cm² | 4.28 - 9.99 ft-lb/in² | Average value: 1.38 J/cm² Grade Count:12 |
| 0.600 - 1.10 J/cm² @Temperature -30.0 - 0.000 °C | 2.86 - 5.24 ft-lb/in² @Temperature -22.0 - 32.0 °F | Average value: 0.900 J/cm² Grade Count:12 | |
| Tensile Creep Modulus, 1 hour | 2200 - 9600 MPa | 319000 - 1.39e+6 psi | Average value: 3550 MPa Grade Count:6 |
| Tensile Creep Modulus, 1000 hours | 800 - 5200 MPa | 116000 - 754000 psi | Average value: 1880 MPa Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+15 ohm-cm | 1.00e+12 - 1.00e+15 ohm-cm | Average value: 5.25e+14 ohm-cm Grade Count:12 |
| Surface Resistance | 1.00e+13 - 1.00e+15 ohm | 1.00e+13 - 1.00e+15 ohm | Average value: 4.06e+14 ohm Grade Count:9 |
| Dielectric Constant | 3.30 - 10.0 | 3.30 - 10.0 | Average value: 4.81 Grade Count:11 |
| Dielectric Strength | 19.0 - 35.0 kV/mm | 483 - 889 kV/in | Average value: 26.6 kV/mm Grade Count:12 |
| Dissipation Factor | 0.00500 - 0.300 | 0.00500 - 0.300 | Average value: 0.0640 Grade Count:12 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 575 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 70.0 µm/m-°C | 11.1 - 38.9 µin/in-°F | Average value: 41.3 µm/m-°C Grade Count:9 |
| CTE, linear, Transverse to Flow | 38.0 - 70.0 µm/m-°C | 21.1 - 38.9 µin/in-°F | Average value: 59.1 µm/m-°C Grade Count:9 |
| Melting Point | 260 °C | 500 °F | Average value: 260 °C Grade Count:7 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 - 260 °C | 185 - 500 °F | Average value: 184 °C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 - 255 °C | 167 - 491 °F | Average value: 163 °C Grade Count:8 |
| Vicat Softening Point | 99.0 - 230 °C | 210 - 446 °F | Average value: 150 °C Grade Count:6 |
| Glass Transition Temp, Tg | 93.0 - 153 °C | 199 - 307 °F | Average value: 131 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 65.0 - 80.0 °C | 149 - 176 °F | Average value: 72.5 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 65.0 - 85.0 °C | 149 - 185 °F | Average value: 75.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:8 |
| Glow Wire Test | 850 °C | 1560 °F | Average value: 850 °C Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:4 |