  4. DuPont Performance Polymers Zytel® 158 NC010 Nylon 612

DuPont Performance Polymers Zytel® 158 NC010 Nylon 612

DuPont Performance Polymers Zytel® 158 NC010 Nylon 612 物性表: DuPont Performance Polymers Zytel® 158 NC010 Nylon 612物性表及特性介绍,DuPont Performance Polymers Zytel® 158 NC010 Nylon 612注塑参数详情,如需DuPont Performance Polymers Zytel® 158 NC010 Nylon 612下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.06
  • 吸水率 [%]: 0.25
  • 成型收缩率 [%]: 0.011
  • 缺口冲击强度: 0.32
  • 拉伸强度 [MPa]: 17.0
  • 弯曲模量 [MPa]: 0.300
  • 硬度: 108.0
  • 热变形温度 [℃]: 135.0
  • 脆化温度 [℃]: -126.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.06 g/cc1.06 g/ccDAM; ASTM D792
Density 1.06 g/cc0.0383 lb/in³DAM; ASTM D792
 1.06 g/cc0.0383 lb/in³DAM; ISO 1183
Water Absorption  0.25 %
@Temperature 23.0 °C		0.25 %
@Temperature 73.4 °F		Immersion 24h; DAM; ASTM D570
 1.3 %
@Temperature 23.0 °C		1.3 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation; DAM; ASTM D570
 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.011 cm/cm
@Thickness 3.20 mm		0.011 in/in
@Thickness 0.126 in		Flow; DAM
 0.011 cm/cm
@Thickness 3.20 mm		0.011 in/in
@Thickness 0.126 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.015 cm/cm
@Thickness 2.00 mm		0.015 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm
@Thickness 2.00 mm		0.015 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 10810850%RH; ASTM D785
 10810850%RH; ISO 2039/2
 114114DAM; ASTM D785
 114114DAM; ISO 2039/2
Tensile Strength  30.0 MPa
@Temperature 121 °C		4350 psi
@Temperature 250 °F		50%RH; ASTM D638
 37.0 MPa
@Temperature 77.0 °C		5370 psi
@Temperature 171 °F		50%RH; ASTM D638
 41.0 MPa
@Temperature 77.0 °C		5950 psi
@Temperature 171 °F		DAM; ASTM D638
 51.0 MPa
@Temperature 23.0 °C		7400 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 93.0 MPa
@Temperature -40.0 °C		13500 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Tensile Stress  6.65 MPa
@Strain 2.70 %,
Temperature 120 °C		965 psi
@Strain 2.70 %,
Temperature 248 °F		DAM; ISO 527
 7.71 MPa
@Strain 2.90 %,
Temperature 120 °C		1120 psi
@Strain 2.90 %,
Temperature 248 °F		50%RH; ISO 527
 9.30 MPa
@Strain 2.55 %,
Temperature 90.0 °C		1350 psi
@Strain 2.55 %,
Temperature 194 °F		DAM; ISO 527
 10.0 MPa
@Strain 2.57 %,
Temperature 90.0 °C		1450 psi
@Strain 2.57 %,
Temperature 194 °F		50%RH; ISO 527
 11.2 MPa
@Strain 5.40 %,
Temperature 120 °C		1620 psi
@Strain 5.40 %,
Temperature 248 °F		DAM; ISO 527
 11.2 MPa
@Strain 0.380 %,
Temperature 23.0 °C		1620 psi
@Strain 0.380 %,
Temperature 73.4 °F		DAM; ISO 527
 12.5 MPa
@Strain 5.80 %,
Temperature 120 °C		1810 psi
@Strain 5.80 %,
Temperature 248 °F		50%RH; ISO 527
 12.9 MPa
@Strain 2.55 %,
Temperature 60.0 °C		1870 psi
@Strain 2.55 %,
Temperature 140 °F		50%RH; ISO 527
 14.0 MPa
@Strain 0.450 %,
Temperature 0.000 °C		2030 psi
@Strain 0.450 %,
Temperature 32.0 °F		DAM; ISO 527
 14.3 MPa
@Strain 8.10 %,
Temperature 120 °C		2070 psi
@Strain 8.10 %,
Temperature 248 °F		DAM; ISO 527
 15.0 MPa
@Strain 2.85 %,
Temperature 60.0 °C		2180 psi
@Strain 2.85 %,
Temperature 140 °F		DAM; ISO 527
 15.2 MPa
@Strain 5.14 %,
Temperature 90.0 °C		2200 psi
@Strain 5.14 %,
Temperature 194 °F		50%RH; ISO 527
 15.6 MPa
@Strain 5.10 %,
Temperature 90.0 °C		2260 psi
@Strain 5.10 %,
Temperature 194 °F		DAM; ISO 527
 15.7 MPa
@Strain 8.70 %,
Temperature 120 °C		2280 psi
@Strain 8.70 %,
Temperature 248 °F		50%RH; ISO 527
 16.0 MPa
@Strain 2.30 %,
Temperature 40.0 °C		2320 psi
@Strain 2.30 %,
Temperature 104 °F		50%RH; ISO 527
 16.3 MPa
@Strain 10.8 %,
Temperature 120 °C		2360 psi
@Strain 10.8 %,
Temperature 248 °F		DAM; ISO 527
 17.5 MPa
@Strain 11.6 %,
Temperature 120 °C		2540 psi
@Strain 11.6 %,
Temperature 248 °F		50%RH; ISO 527
 17.5 MPa
@Strain 13.5 %,
Temperature 120 °C		2540 psi
@Strain 13.5 %,
Temperature 248 °F		DAM; ISO 527
 18.1 MPa
@Strain 16.2 %,
Temperature 120 °C		2630 psi
@Strain 16.2 %,
Temperature 248 °F		DAM; ISO 527
 18.5 MPa
@Strain 14.5 %,
Temperature 120 °C		2680 psi
@Strain 14.5 %,
Temperature 248 °F		50%RH; ISO 527
 18.6 MPa
@Strain 18.9 %,
Temperature 120 °C		2700 psi
@Strain 18.9 %,
Temperature 248 °F		DAM; ISO 527
 18.7 MPa
@Strain 7.71 %,
Temperature 90.0 °C		2710 psi
@Strain 7.71 %,
Temperature 194 °F		50%RH; ISO 527
 18.8 MPa
@Strain 17.4 %,
Temperature 120 °C		2730 psi
@Strain 17.4 %,
Temperature 248 °F		50%RH; ISO 527
 19.1 MPa
@Strain 20.3 %,
Temperature 120 °C		2770 psi
@Strain 20.3 %,
Temperature 248 °F		50%RH; ISO 527
 19.1 MPa
@Strain 21.6 %,
Temperature 120 °C		2770 psi
@Strain 21.6 %,
Temperature 248 °F		DAM; ISO 527
 19.3 MPa
@Strain 23.2 %,
Temperature 120 °C		2800 psi
@Strain 23.2 %,
Temperature 248 °F		50%RH; ISO 527
 19.5 MPa
@Strain 24.3 %,
Temperature 120 °C		2830 psi
@Strain 24.3 %,
Temperature 248 °F		DAM; ISO 527
 19.7 MPa
@Strain 26.1 %,
Temperature 120 °C		2860 psi
@Strain 26.1 %,
Temperature 248 °F		50%RH; ISO 527
 19.8 MPa
@Strain 7.65 %,
Temperature 90.0 °C		2870 psi
@Strain 7.65 %,
Temperature 194 °F		DAM; ISO 527
 19.9 MPa
@Strain 27.0 %,
Temperature 120 °C		2890 psi
@Strain 27.0 %,
Temperature 248 °F		DAM; Break; ISO 527
 20.0 MPa
@Strain 29.0 %,
Temperature 120 °C		2900 psi
@Strain 29.0 %,
Temperature 248 °F		50%RH; Break; ISO 527
 20.6 MPa
@Strain 10.3 %,
Temperature 90.0 °C		2990 psi
@Strain 10.3 %,
Temperature 194 °F		50%RH; ISO 527
 20.9 MPa
@Strain 5.10 %,
Temperature 60.0 °C		3030 psi
@Strain 5.10 %,
Temperature 140 °F		50%RH; ISO 527
 20.9 MPa
@Strain 0.760 %,
Temperature 23.0 °C		3030 psi
@Strain 0.760 %,
Temperature 73.4 °F		DAM; ISO 527
 21.7 MPa
@Strain 12.9 %,
Temperature 90.0 °C		3150 psi
@Strain 12.9 %,
Temperature 194 °F		50%RH; ISO 527
 22.3 MPa
@Strain 10.2 %,
Temperature 90.0 °C		3230 psi
@Strain 10.2 %,
Temperature 194 °F		DAM; ISO 527
 22.6 MPa
@Strain 15.4 %,
Temperature 90.0 °C		3280 psi
@Strain 15.4 %,
Temperature 194 °F		50%RH; ISO 527
 23.2 MPa
@Strain 18.0 %,
Temperature 90.0 °C		3360 psi
@Strain 18.0 %,
Temperature 194 °F		50%RH; ISO 527
 23.6 MPa
@Strain 12.8 %,
Temperature 90.0 °C		3420 psi
@Strain 12.8 %,
Temperature 194 °F		DAM; ISO 527
 23.7 MPa
@Strain 20.6 %,
Temperature 90.0 °C		3440 psi
@Strain 20.6 %,
Temperature 194 °F		50%RH; ISO 527
 24.0 MPa
@Strain 23.1 %,
Temperature 90.0 °C		3480 psi
@Strain 23.1 %,
Temperature 194 °F		50%RH; ISO 527
 24.0 MPa
@Strain 5.70 %,
Temperature 60.0 °C		3480 psi
@Strain 5.70 %,
Temperature 140 °F		DAM; ISO 527
 24.3 MPa
@Strain 25.7 %,
Temperature 90.0 °C		3520 psi
@Strain 25.7 %,
Temperature 194 °F		50%RH; Break; ISO 527
 24.3 MPa
@Strain 15.3 %,
Temperature 90.0 °C		3520 psi
@Strain 15.3 %,
Temperature 194 °F		DAM; ISO 527
 24.8 MPa
@Strain 17.9 %,
Temperature 90.0 °C		3600 psi
@Strain 17.9 %,
Temperature 194 °F		DAM; ISO 527
 25.4 MPa
@Strain 20.4 %,
Temperature 90.0 °C		3680 psi
@Strain 20.4 %,
Temperature 194 °F		DAM; ISO 527
 25.7 MPa
@Strain 23.0 %,
Temperature 90.0 °C		3730 psi
@Strain 23.0 %,
Temperature 194 °F		DAM; ISO 527
 25.7 MPa
@Strain 4.60 %,
Temperature 40.0 °C		3730 psi
@Strain 4.60 %,
Temperature 104 °F		50%RH; ISO 527
 25.9 MPa
@Strain 25.5 %,
Temperature 90.0 °C		3760 psi
@Strain 25.5 %,
Temperature 194 °F		DAM; Break; ISO 527
 26.3 MPa
@Strain 7.65 %,
Temperature 60.0 °C		3810 psi
@Strain 7.65 %,
Temperature 140 °F		50%RH; ISO 527
 26.3 MPa
@Strain 0.900 %,
Temperature 0.000 °C		3810 psi
@Strain 0.900 %,
Temperature 32.0 °F		DAM; ISO 527
 26.8 MPa
@Strain 1.85 %,
Temperature 23.0 °C		3890 psi
@Strain 1.85 %,
Temperature 73.4 °F		50%RH; ISO 527
 28.5 MPa
@Strain 8.55 %,
Temperature 60.0 °C		4130 psi
@Strain 8.55 %,
Temperature 140 °F		DAM; ISO 527
 29.5 MPa
@Strain 10.2 %,
Temperature 60.0 °C		4280 psi
@Strain 10.2 %,
Temperature 140 °F		50%RH; ISO 527
 29.5 MPa
@Strain 1.14 %,
Temperature 23.0 °C		4280 psi
@Strain 1.14 %,
Temperature 73.4 °F		DAM; ISO 527
 30.0 MPa
@Strain 1.15 %,
Temperature -20.0 °C		4350 psi
@Strain 1.15 %,
Temperature -4.00 °F		50%RH; ISO 527
 31.0 MPa
@Strain 11.4 %,
Temperature 60.0 °C		4500 psi
@Strain 11.4 %,
Temperature 140 °F		DAM; ISO 527
 31.1 MPa
@Strain 12.8 %,
Temperature 60.0 °C		4510 psi
@Strain 12.8 %,
Temperature 140 °F		50%RH; ISO 527
 31.6 MPa
@Strain 15.3 %,
Temperature 60.0 °C		4580 psi
@Strain 15.3 %,
Temperature 140 °F		50%RH; ISO 527
 31.9 MPa
@Strain 17.9 %,
Temperature 60.0 °C		4630 psi
@Strain 17.9 %,
Temperature 140 °F		50%RH; ISO 527
 32.0 MPa
@Strain 14.3 %,
Temperature 60.0 °C		4640 psi
@Strain 14.3 %,
Temperature 140 °F		DAM; ISO 527
 32.0 MPa
@Strain 5.60 %,
Temperature 40.0 °C		4640 psi
@Strain 5.60 %,
Temperature 104 °F		DAM; ISO 527
 32.1 MPa
@Strain 6.90 %,
Temperature 40.0 °C		4660 psi
@Strain 6.90 %,
Temperature 104 °F		50%RH; ISO 527
 32.1 MPa
@Strain 20.4 %,
Temperature 60.0 °C		4660 psi
@Strain 20.4 %,
Temperature 140 °F		50%RH; ISO 527
 32.2 MPa
@Strain 23.0 %,
Temperature 60.0 °C		4670 psi
@Strain 23.0 %,
Temperature 140 °F		50%RH; ISO 527
 32.3 MPa
@Strain 25.5 %,
Temperature 60.0 °C		4680 psi
@Strain 25.5 %,
Temperature 140 °F		50%RH; Break; ISO 527
 32.5 MPa
@Strain 17.1 %,
Temperature 60.0 °C		4710 psi
@Strain 17.1 %,
Temperature 140 °F		DAM; ISO 527
 33.0 MPa
@Strain 20.0 %,
Temperature 60.0 °C		4790 psi
@Strain 20.0 %,
Temperature 140 °F		DAM; ISO 527
 33.3 MPa
@Strain 22.8 %,
Temperature 60.0 °C		4830 psi
@Strain 22.8 %,
Temperature 140 °F		DAM; ISO 527
 33.7 MPa
@Strain 25.7 %,
Temperature 60.0 °C		4890 psi
@Strain 25.7 %,
Temperature 140 °F		DAM; ISO 527
 34.0 MPa
@Strain 28.5 %,
Temperature 60.0 °C		4930 psi
@Strain 28.5 %,
Temperature 140 °F		DAM; Break; ISO 527
 34.6 MPa
@Strain 1.45 %,
Temperature 0.000 °C		5020 psi
@Strain 1.45 %,
Temperature 32.0 °F		50%RH; ISO 527
 35.9 MPa
@Strain 9.20 %,
Temperature 40.0 °C		5210 psi
@Strain 9.20 %,
Temperature 104 °F		50%RH; ISO 527
 36.9 MPa
@Strain 1.52 %,
Temperature 23.0 °C		5350 psi
@Strain 1.52 %,
Temperature 73.4 °F		DAM; ISO 527
 37.2 MPa
@Strain 1.35 %,
Temperature 0.000 °C		5400 psi
@Strain 1.35 %,
Temperature 32.0 °F		DAM; ISO 527
 37.8 MPa
@Strain 11.5 %,
Temperature 40.0 °C		5480 psi
@Strain 11.5 %,
Temperature 104 °F		50%RH; ISO 527
 37.9 MPa
@Strain 3.70 %,
Temperature 23.0 °C		5500 psi
@Strain 3.70 %,
Temperature 73.4 °F		50%RH; ISO 527
 38.7 MPa
@Strain 13.8 %,
Temperature 40.0 °C		5610 psi
@Strain 13.8 %,
Temperature 104 °F		50%RH; ISO 527
 39.0 MPa
@Strain 8.20 %,
Temperature 40.0 °C		5660 psi
@Strain 8.20 %,
Temperature 104 °F		DAM; ISO 527
 39.1 MPa
@Strain 16.1 %,
Temperature 40.0 °C		5670 psi
@Strain 16.1 %,
Temperature 104 °F		50%RH; ISO 527
 39.5 MPa
@Strain 18.4 %,
Temperature 40.0 °C		5730 psi
@Strain 18.4 %,
Temperature 104 °F		50%RH; ISO 527
 39.9 MPa
@Strain 20.7 %,
Temperature 40.0 °C		5790 psi
@Strain 20.7 %,
Temperature 104 °F		50%RH; ISO 527
 40.1 MPa
@Strain 23.0 %,
Temperature 40.0 °C		5820 psi
@Strain 23.0 %,
Temperature 104 °F		50%RH; Break; ISO 527
 41.5 MPa
@Strain 10.8 %,
Temperature 40.0 °C		6020 psi
@Strain 10.8 %,
Temperature 104 °F		DAM; ISO 527
 42.7 MPa
@Strain 5.55 %,
Temperature 23.0 °C		6190 psi
@Strain 5.55 %,
Temperature 73.4 °F		50%RH; ISO 527
 42.8 MPa
@Strain 13.4 %,
Temperature 40.0 °C		6210 psi
@Strain 13.4 %,
Temperature 104 °F		DAM; ISO 527
 43.0 MPa
@Strain 1.90 %,
Temperature 23.0 °C		6240 psi
@Strain 1.90 %,
Temperature 73.4 °F		DAM; ISO 527
 43.6 MPa
@Strain 16.0 %,
Temperature 40.0 °C		6320 psi
@Strain 16.0 %,
Temperature 104 °F		DAM; ISO 527
 44.4 MPa
@Strain 18.6 %,
Temperature 40.0 °C		6440 psi
@Strain 18.6 %,
Temperature 104 °F		DAM; ISO 527
 44.9 MPa
@Strain 21.2 %,
Temperature 40.0 °C		6510 psi
@Strain 21.2 %,
Temperature 104 °F		DAM; ISO 527
 44.9 MPa
@Strain 7.40 %,
Temperature 23.0 °C		6510 psi
@Strain 7.40 %,
Temperature 73.4 °F		50%RH; ISO 527
 45.4 MPa
@Strain 23.8 %,
Temperature 40.0 °C		6580 psi
@Strain 23.8 %,
Temperature 104 °F		DAM; ISO 527
 45.7 MPa
@Strain 26.4 %,
Temperature 40.0 °C		6630 psi
@Strain 26.4 %,
Temperature 104 °F		DAM; ISO 527
 46.0 MPa
@Strain 29.0 %,
Temperature 40.0 °C		6670 psi
@Strain 29.0 %,
Temperature 104 °F		DAM; Break; ISO 527
 46.3 MPa
@Strain 9.25 %,
Temperature 23.0 °C		6720 psi
@Strain 9.25 %,
Temperature 73.4 °F		50%RH; ISO 527
 46.7 MPa
@Strain 1.80 %,
Temperature 0.000 °C		6770 psi
@Strain 1.80 %,
Temperature 32.0 °F		DAM; ISO 527
 47.3 MPa
@Strain 11.1 %,
Temperature 23.0 °C		6860 psi
@Strain 11.1 %,
Temperature 73.4 °F		50%RH; ISO 527
 48.0 MPa
@Strain 13.0 %,
Temperature 23.0 °C		6960 psi
@Strain 13.0 %,
Temperature 73.4 °F		50%RH; ISO 527
 48.0 MPa
@Strain 2.28 %,
Temperature 23.0 °C		6960 psi
@Strain 2.28 %,
Temperature 73.4 °F		DAM; ISO 527
 48.7 MPa
@Strain 14.8 %,
Temperature 23.0 °C		7060 psi
@Strain 14.8 %,
Temperature 73.4 °F		50%RH; ISO 527
 49.2 MPa
@Strain 16.7 %,
Temperature 23.0 °C		7140 psi
@Strain 16.7 %,
Temperature 73.4 °F		50%RH; ISO 527
 49.5 MPa
@Strain 18.5 %,
Temperature 23.0 °C		7180 psi
@Strain 18.5 %,
Temperature 73.4 °F		50%RH; Break; ISO 527
 50.0 MPa
@Strain 2.30 %,
Temperature -20.0 °C		7250 psi
@Strain 2.30 %,
Temperature -4.00 °F		50%RH; ISO 527
 51.8 MPa
@Strain 2.66 %,
Temperature 23.0 °C		7510 psi
@Strain 2.66 %,
Temperature 73.4 °F		DAM; ISO 527
 52.3 MPa
@Strain 2.90 %,
Temperature 0.000 °C		7590 psi
@Strain 2.90 %,
Temperature 32.0 °F		50%RH; ISO 527
 54.6 MPa
@Strain 3.04 %,
Temperature 23.0 °C		7920 psi
@Strain 3.04 %,
Temperature 73.4 °F		DAM; ISO 527
 54.8 MPa
@Strain 2.25 %,
Temperature 0.000 °C		7950 psi
@Strain 2.25 %,
Temperature 32.0 °F		DAM; ISO 527
 56.2 MPa
@Strain 3.42 %,
Temperature 23.0 °C		8150 psi
@Strain 3.42 %,
Temperature 73.4 °F		DAM; ISO 527
 56.8 MPa
@Strain 3.80 %,
Temperature 23.0 °C		8240 psi
@Strain 3.80 %,
Temperature 73.4 °F		DAM; Break; ISO 527
 60.4 MPa
@Strain 4.35 %,
Temperature 0.000 °C		8760 psi
@Strain 4.35 %,
Temperature 32.0 °F		50%RH; ISO 527
 61.6 MPa
@Strain 2.70 %,
Temperature 0.000 °C		8930 psi
@Strain 2.70 %,
Temperature 32.0 °F		DAM; ISO 527
 62.1 MPa
@Strain 3.45 %,
Temperature -20.0 °C		9010 psi
@Strain 3.45 %,
Temperature -4.00 °F		50%RH; ISO 527
 63.1 MPa
@Strain 5.80 %,
Temperature 0.000 °C		9150 psi
@Strain 5.80 %,
Temperature 32.0 °F		50%RH; ISO 527
 64.3 MPa
@Strain 7.25 %,
Temperature 0.000 °C		9330 psi
@Strain 7.25 %,
Temperature 32.0 °F		50%RH; ISO 527
 64.9 MPa
@Strain 8.70 %,
Temperature 0.000 °C		9410 psi
@Strain 8.70 %,
Temperature 32.0 °F		50%RH; ISO 527
 65.3 MPa
@Strain 10.2 %,
Temperature 0.000 °C		9470 psi
@Strain 10.2 %,
Temperature 32.0 °F		50%RH; ISO 527
 65.6 MPa
@Strain 11.6 %,
Temperature 0.000 °C		9510 psi
@Strain 11.6 %,
Temperature 32.0 °F		50%RH; ISO 527
 65.8 MPa
@Strain 13.1 %,
Temperature 0.000 °C		9540 psi
@Strain 13.1 %,
Temperature 32.0 °F		50%RH; ISO 527
 66.0 MPa
@Strain 14.5 %,
Temperature 0.000 °C		9570 psi
@Strain 14.5 %,
Temperature 32.0 °F		50%RH; Break; ISO 527
 66.8 MPa
@Strain 3.15 %,
Temperature 0.000 °C		9690 psi
@Strain 3.15 %,
Temperature 32.0 °F		DAM; ISO 527
 68.0 MPa
@Strain 4.60 %,
Temperature -20.0 °C		9860 psi
@Strain 4.60 %,
Temperature -4.00 °F		50%RH; ISO 527
 70.5 MPa
@Strain 3.60 %,
Temperature 0.000 °C		10200 psi
@Strain 3.60 %,
Temperature 32.0 °F		DAM; ISO 527
 71.1 MPa
@Strain 5.75 %,
Temperature -20.0 °C		10300 psi
@Strain 5.75 %,
Temperature -4.00 °F		50%RH; ISO 527
 72.5 MPa
@Strain 6.90 %,
Temperature -20.0 °C		10500 psi
@Strain 6.90 %,
Temperature -4.00 °F		50%RH; ISO 527
 72.6 MPa
@Strain 4.05 %,
Temperature 0.000 °C		10500 psi
@Strain 4.05 %,
Temperature 32.0 °F		DAM; ISO 527
 73.1 MPa
@Strain 4.50 %,
Temperature 0.000 °C		10600 psi
@Strain 4.50 %,
Temperature 32.0 °F		DAM; Break; ISO 527
 73.4 MPa
@Strain 8.05 %,
Temperature -20.0 °C		10600 psi
@Strain 8.05 %,
Temperature -4.00 °F		50%RH; ISO 527
 73.7 MPa
@Strain 9.20 %,
Temperature -20.0 °C		10700 psi
@Strain 9.20 %,
Temperature -4.00 °F		50%RH; ISO 527
 73.9 MPa
@Strain 10.4 %,
Temperature -20.0 °C		10700 psi
@Strain 10.4 %,
Temperature -4.00 °F		50%RH; ISO 527
 74.0 MPa
@Strain 11.5 %,
Temperature -20.0 °C		10700 psi
@Strain 11.5 %,
Temperature -4.00 °F		50%RH; Break; ISO 527
Tensile Strength, Yield  17.0 MPa
@Temperature 121 °C		2470 psi
@Temperature 250 °F		50%RH; ASTM D638
 26.0 MPa
@Temperature 77.0 °C		3770 psi
@Temperature 171 °F		50%RH; ASTM D638
 30.0 MPa
@Temperature 77.0 °C		4350 psi
@Temperature 171 °F		DAM; ASTM D638
 51.0 MPa
@Temperature 23.0 °C		7400 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 52.0 MPa
@Temperature 23.0 °C		7540 psi
@Temperature 73.4 °F		50%RH; ISO 527
 61.0 MPa
@Temperature 23.0 °C		8850 psi
@Temperature 73.4 °F		DAM; ASTM D638
 62.0 MPa
@Temperature 23.0 °C		8990 psi
@Temperature 73.4 °F		DAM; ISO 527
 93.0 MPa
@Temperature -40.0 °C		13500 psi
@Temperature -40.0 °F		50%RH; ASTM D638
 94.0 MPa
@Temperature -40.0 °C		13600 psi
@Temperature -40.0 °F		DAM; ASTM D638
Elongation at Break  15 %
@Temperature -40.0 °C		15 %
@Temperature -40.0 °F		DAM; ASTM D638
 30 %
@Temperature -40.0 °C		30 %
@Temperature -40.0 °F		50%RH; ASTM D638
 35 %
@Temperature 23.0 °C		35 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 >= 50 %
@Temperature 23.0 °C		>= 50 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 150 %
@Temperature 23.0 °C		150 %
@Temperature 73.4 °F		DAM; ASTM D638
 250 %
@Temperature 121 °C		250 %
@Temperature 250 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 23.0 °C		>= 300 %
@Temperature 73.4 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		50%RH; ASTM D638
 >= 300 %
@Temperature 77.0 °C		>= 300 %
@Temperature 171 °F		DAM; ASTM D638
Elongation at Yield  4.3 %
@Temperature 23.0 °C		4.3 %
@Temperature 73.4 °F		DAM; ISO 527
 7.0 %
@Temperature 23.0 °C		7.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 8.0 %
@Temperature -40.0 °C		8.0 %
@Temperature -40.0 °F		DAM; ASTM D638
 14 %
@Temperature -40.0 °C		14 %
@Temperature -40.0 °F		50%RH; ASTM D638
 19 %
@Temperature 23.0 °C		19 %
@Temperature 73.4 °F		50%RH; ISO 527
 30 %
@Temperature 77.0 °C		30 %
@Temperature 171 °F		DAM; ASTM D638
 40 %
@Temperature 23.0 °C		40 %
@Temperature 73.4 °F		50%RH; ASTM D638
Tensile Modulus  1.50 GPa
@Temperature 23.0 °C		218 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 2.40 GPa
@Temperature 23.0 °C		348 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  0.300 GPa
@Temperature 121 °C		43.5 ksi
@Temperature 250 °F		DAM; ASTM D790
 0.300 GPa
@Temperature 121 °C		43.5 ksi
@Temperature 250 °F		50%RH; ASTM D790
 0.380 GPa
@Temperature 77.0 °C		55.1 ksi
@Temperature 171 °F		50%RH; ASTM D790
 0.410 GPa
@Temperature 77.0 °C		59.5 ksi
@Temperature 171 °F		DAM; ASTM D790
 1.24 GPa
@Temperature 23.0 °C		180 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 2.03 GPa
@Temperature 23.0 °C		294 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 2.34 GPa
@Temperature -40.0 °C		339 ksi
@Temperature -40.0 °F		DAM; ASTM D790
 2.76 GPa
@Temperature -40.0 °C		400 ksi
@Temperature -40.0 °F		50%RH; ASTM D790
Shear Strength  56.0 MPa
@Temperature 23.0 °C		8120 psi
@Temperature 73.4 °F		50%RH; ASTM D732
 59.0 MPa
@Temperature 23.0 °C		8560 psi
@Temperature 73.4 °F		DAM; ASTM D732
Izod Impact, Notched  0.320 J/cm
@Temperature -40.0 °C		0.599 ft-lb/in
@Temperature -40.0 °F		50%RH; ASTM D256
 0.480 J/cm
@Temperature -40.0 °C		0.899 ft-lb/in
@Temperature -40.0 °F		DAM; ASTM D256
 0.530 J/cm
@Temperature 23.0 °C		0.993 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 0.750 J/cm
@Temperature 23.0 °C		1.41 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Notched (ISO)  4.00 kJ/m²
@Temperature 23.0 °C		1.90 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 4.50 kJ/m²
@Temperature -30.0 °C		2.14 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 6.00 kJ/m²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact Unnotched  NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 NB
@Temperature -30.0 °C		NB
@Temperature -22.0 °F		DAM; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 NB
@Temperature 23.0 °C		NB
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm²
@Temperature -30.0 °C		1.90 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 0.420 J/cm²
@Temperature -30.0 °C		2.00 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 0.420 J/cm²
@Temperature 23.0 °C		2.00 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 0.800 J/cm²
@Temperature 23.0 °C		3.81 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Impact Strength  153 kJ/m²
@Temperature 23.0 °C		72.8 ft-lb/in²
@Temperature 73.4 °F		DAM; Short specimen; ASTM D1822
 218 kJ/m²
@Temperature 23.0 °C		104 ft-lb/in²
@Temperature 73.4 °F		50%RH; Short specimen; ASTM D1822
 611 kJ/m²
@Temperature 23.0 °C		291 ft-lb/in²
@Temperature 73.4 °F		DAM; Long specimen; ASTM D1822
 945 kJ/m²
@Temperature 23.0 °C		450 ft-lb/in²
@Temperature 73.4 °F		50%RH; Long specimen; ASTM D1822
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		50%RH; IEC 60093
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; ASTM D257
 >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
 1.00e+17 ohm-cm
@Temperature 23.0 °C		1.00e+17 ohm-cm
@Temperature 73.4 °F		DAM; IEC 60093
Surface Resistance 1.00e+12 ohm
@Temperature 23.0 °C		1.00e+12 ohm
@Temperature 73.4 °F		DAM; IEC 60093
Dielectric Constant  3.2
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.2
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 3.6
@Frequency 100 Hz,
Temperature 23.0 °C		3.6
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 100 Hz,
Temperature 23.0 °C		4.0
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 1000 Hz,
Temperature 23.0 °C		4.0
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 4.0
@Frequency 1000 Hz,
Temperature 23.0 °C		4.0
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 4.0
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		4.0
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 5.3
@Frequency 1000 Hz,
Temperature 23.0 °C		5.3
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 5.3
@Frequency 1000 Hz,
Temperature 23.0 °C		5.3
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 6.0
@Frequency 100 Hz,
Temperature 23.0 °C		6.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 6.0
@Frequency 100 Hz,
Temperature 23.0 °C		6.0
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Dissipation Factor  0.014
@Frequency 100 Hz,
Temperature 23.0 °C		0.014
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.0165
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.0165
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.020
@Frequency 100 Hz,
Temperature 23.0 °C		0.020
@Frequency 100 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		DAM; ASTM D150
 0.020
@Frequency 1000 Hz,
Temperature 23.0 °C		0.020
@Frequency 1000 Hz,
Temperature 73.4 °F		DAM; IEC 60250
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.10
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.10
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.15
@Frequency 100 Hz,
Temperature 23.0 °C		0.15
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.15
@Frequency 1000 Hz,
Temperature 23.0 °C		0.15
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; ASTM D150
 0.15
@Frequency 100 Hz,
Temperature 23.0 °C		0.15
@Frequency 100 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
 0.15
@Frequency 1000 Hz,
Temperature 23.0 °C		0.15
@Frequency 1000 Hz,
Temperature 73.4 °F		50%RH; IEC 60250
Comparative Tracking Index >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 500 µm/m-°C278 µin/in-°FDAM; ASTM D696
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
Melting Point 218 °C424 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 135 °C275 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C131 °FDAM; ASTM D648
 62.0 °C144 °FDAM; ISO 75-1/-2
Brittleness Temperature -126 °C-195 °FDAM; ASTM D746
 -109 °C-164 °F50%RH; ASTM D746
UL RTI, Electrical  105 °C
@Thickness 0.860 mm		221 °F
@Thickness 0.0339 in		DAM; UL 746B
 105 °C
@Thickness 1.50 mm		221 °F
@Thickness 0.0591 in		DAM; UL 746B
 105 °C
@Thickness 3.00 mm		221 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 0.860 mm		149 °F
@Thickness 0.0339 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.860 mm		HB
@Thickness 0.0339 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.860 mm		HB
@Thickness 0.0339 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
Oxygen Index 25 %25 %DAM; ASTM D2863
 25 %25 %DAM; ISO 4589-1/-2
 28 %28 %50%RH; ASTM D2863
 
Processing PropertiesMetricEnglishComments
Melt Temperature 218 °C424 °F10°C/min; DAM; ISO 11357-1/-3
 235 °C455 °FDAM; Optimum; Extrusion
 230 - 240 °C446 - 464 °FDAM; Extrusion
 250 °C482 °FDAM; Optimum; Injection Molding
 230 - 290 °C446 - 554 °FDAM; Injection Molding
Mold Temperature 70.0 °C158 °FDAM; optimum; Injection Molding
 50.0 - 90.0 °C122 - 194 °FDAM; Injection Molding
Drying Temperature 80.0 °C176 °FDAM; Extrusion
 80.0 °C176 °FDAM; Injection Molding
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM; Injection Molding
 4.00 - 6.00 hour4.00 - 6.00 hourDAM; Extrusion
Moisture Content <= 0.050 %<= 0.050 %DAM; Extrusion
 <= 0.050 %<= 0.050 %DAM; Injection Molding
 
Descriptive Properties
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesViscosity, HighDAM
 Viscosity, MediumDAM
FormsPelletsDAM
GenericNylon 612DAM
Material StatusCurrentDAM
Part Marking Code>PA612<ISO 11469; DAM
Processing MethodExtrusionDAM
 ExtrusionDAM
 Injection MoldingDAM
Product CategoryExtrusion ResinsDAM
 Unreinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA612ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47484.html

免责声明: 本文 DuPont Performance Polymers Zytel® 158 NC010 Nylon 612 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4