- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 2.8
- 拉伸强度 [MPa]: 50.0
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | ||
| Water Absorption | 2.8 % | 2.8 % | ISO 62 | ||
| Moisture Absorption | 1.30 % | 1.30 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 76 | 76 | conditioned, 15s; ISO 868 | ||
| 81 | 81 | dry, 15s; ISO 868 | |||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | conditioned; ISO 527-1/-2 | ||
| 60.0 MPa | 8700 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | <= 50 % | <= 50 % | dry; ISO 527-1/-2 | ||
| >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 16 % | 16 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 1.60 GPa | 232 ksi | conditioned; ISO 527-1/-2 | ||
| 2.30 GPa | 334 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.00 J/cm² | 4.76 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 30.0 °C | 2.86 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.600 J/cm² @Temperature 30.0 °C | 2.86 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | dry; IEC 60093 | ||
| 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | dry; IEC 60243-1 | ||
| 32.0 kV/mm | 813 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 218 °C | 424 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | long term; EMS | ||
| 150 °C | 302 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Mechanical Engineering | |||||
| Tools & Accessories | |||||
| Processing | Film Extrusion | ||||
| Other Extrusion | |||||
| Product Attributes | High viscosity | ||||