- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.3
- 缺口冲击强度: 10.0
- 弯曲模量 [MPa]: 7.00
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| 0.70 % @Temperature 23.0 °C | 0.70 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | |||
| 1.8 % @Temperature 23.0 °C | 1.8 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa @Temperature 23.0 °C | 20300 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 168 MPa @Temperature 23.0 °C | 24400 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 3.2 % @Temperature 23.0 °C | 3.2 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 3.2 % @Temperature 23.0 °C | 3.2 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.90 GPa @Temperature 23.0 °C | 1150 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.50 GPa @Temperature 23.0 °C | 1380 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 7.00 GPa @Temperature 23.0 °C | 1020 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 8.20 GPa @Temperature 23.0 °C | 1190 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 10.0 kJ/m² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature -40.0 °C | 5.23 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | |||
| 11.0 kJ/m² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| 13.0 kJ/m² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1U | ||
| 60.0 kJ/m² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1U | |||
| 60.0 kJ/m² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1U | |||
| 70.0 kJ/m² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | |||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 6.50 J/cm² @Temperature -30.0 °C | 30.9 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -40.0 °C | 4.76 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 179/1eA | |||
| 1.10 J/cm² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| 1.20 J/cm² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 46.1 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 113 µm/m-°C @Temperature 23.0 - 55.0 °C | 62.8 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 158 µm/m-°C @Temperature 55.0 - 160 °C | 87.8 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Forms | Pellets | DAM | |||
| Generic | PA612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612-GF33< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Food Contact Resins | DAM | |||
| Glass Reinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-GF33 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Food Applications, Non-specific | DAM | |||