- 密度 [g/cm3]: 1.342
- 吸水率 [%]: 0.5
- 缺口冲击强度: 0.43
- 断裂伸长率 [%]: 76.0
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 2.07
- 热变形温度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.342 g/cc | 0.04848 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm @Thickness 3.17 mm | 0.010 - 0.020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 2.0 - 5.0 % | 2.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 - 0.690 J/cm @Thickness 6.35 mm | 0.806 - 1.29 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 93.0 - 107 °C | 199 - 225 °F | |