- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 1.9
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | 23°C/50% R.H.; ISO 62 |
| Water Absorption at Saturation | 1.9 % | 1.9 % | ISO 62 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 8.34 GPa | 1210 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 10.4 J/cm² @Temperature 23.0 °C | 49.5 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| 11.0 J/cm² @Temperature -30.0 °C | 52.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ISO 75 |
| Vicat Softening Point | 209 °C | 408 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||