- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.21
- 弯曲模量 [MPa]: 2.75
- 热变形温度 [℃]: 169.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Time 86400 sec | 0.017 in/in @Time 24.0 hour | ASTM D955 |
| 0.017 cm/cm @Time 86400 sec | 0.017 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Time 86400 sec | 0.017 in/in @Time 24.0 hour | ASTM D955 |
| 0.0172 cm/cm @Time 86400 sec | 0.0172 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 |
| 54.0 MPa | 7830 psi | ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| 3.0 % | 3.0 % | ASTM D638 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 50 mm/min; ASTM D638 |
| 3.30 GPa | 479 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| 84.0 MPa | 12200 psi | ISO 178 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| 3.00 GPa | 435 ksi | ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.50 J/cm | 4.68 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C @Thickness 3.20 mm | 336 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 76.0 °C @Thickness 3.20 mm | 169 °F @Thickness 0.126 in | unannealed; ASTM D648 | |