SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12 物性表: SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12物性表及特性介绍,SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12注塑参数详情,如需SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.31
  • 缺口冲击强度: 1.38
  • 弯曲模量 [MPa]: 8.83
  • 热变形温度 [℃]: 213.0
 
Physical PropertiesMetricEnglishComments
Density 1.31 g/cc0.0473 lb/in³ISO 1183
 1.32 g/cc0.0477 lb/in³ASTM D 792
Moisture Absorption at Equilibrium 0.10 %
@Time 86400 sec
0.10 %
@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow  0.0011 - 0.0016 cm/cm
@Time 86400 sec
0.0011 - 0.0016 in/in
@Time 24.0 hour
ISO 294
 0.0010 - 0.0020 cm/cm
@Time 86400 sec
0.0010 - 0.0020 in/in
@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse  0.0066 - 0.0071 cm/cm
@Time 86400 sec
0.0066 - 0.0071 in/in
@Time 24.0 hour
ISO 294
 0.0070 - 0.0080 cm/cm
@Time 86400 sec
0.0070 - 0.0080 in/in
@Time 24.0 hour
ASTM D 955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 178 MPa25800 psiISO 527
 182 MPa26400 psiASTM D 638
Elongation at Break 3.4 %3.4 %ISO 527
 3.7 %3.7 %ASTM D 638
Tensile Modulus 9.58 GPa1390 ksi50 mm/min; ASTM D 638
 10.32 GPa1497 ksi1 mm/min; ISO 527
Flexural Strength 250 MPa36300 psiISO 178
 289 MPa41900 psiASTM D 790
Flexural Modulus 8.83 GPa1280 ksiISO 178
 9.30 GPa1350 ksiASTM D 790
Izod Impact, Notched 1.38 J/cm
@Temperature 23.0 °C
2.59 ft-lb/in
@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 12.28 J/cm
@Temperature 23.0 °C
23.01 ft-lb/in
@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 14.0 kJ/m²
@Temperature 23.0 °C
6.66 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 78.0 kJ/m²
@Temperature 23.0 °C
37.1 ft-lb/in²
@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 3.00 J2.21 ft-lbMultiaxial Impact; ISO 6603
 14.0 J
@Temperature 23.0 °C
10.3 ft-lb
@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  40.5 µm/m-°C
@Temperature -40.0 - 40.0 °C
22.5 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
 41.4 µm/m-°C
@Temperature -40.0 - 40.0 °C
23.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow  73.1 µm/m-°C
@Temperature -40.0 - 40.0 °C
40.6 µin/in-°F
@Temperature -40.0 - 104 °F
ISO 11359-2
 73.8 µm/m-°C
@Temperature -40.0 - 40.0 °C
41.0 µin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 213 °C
@Thickness 3.20 mm
415 °F
@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
@Thickness 3.20 mm
388 °F
@Thickness 0.126 in
unannealed; ASTM D 648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47788.html

免责声明: 本文 SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4