Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12

Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12 物性表: Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12物性表及特性介绍,Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12注塑参数详情,如需Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12下载, 可到相关下载区下载

吸水率 [%]: 0.13
缺口冲击强度: 1.23
弯曲模量 [MPa]: 8.34

Physical Properties	Metric	English	Comments

Specific Gravity	1.42 g/cc	1.42 g/cc	ASTM D792
Water Absorption	0.13 %	0.13 %	24 Hrs; ASTM D570
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	138 MPa	20000 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Strength	197 MPa	28500 psi	ASTM D790
Flexural Modulus	8.34 GPa	1210 ksi	ASTM D790
Compressive Strength	124 MPa	18000 psi	ASTM D695
Izod Impact, Notched	1.23 J/cm	2.30 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	48.6 µm/m-°C @Temperature 20.0 °C	27.0 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	199 °C	390 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0625 in

关键词:
供应
PA612
Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47809.html

免责声明: 本文 Techmer Lehvoss Compounds Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息