- 吸水率 [%]: 0.1
- 缺口冲击强度: 1.39
- 拉伸强度 [MPa]: 182.0
- 弯曲模量 [MPa]: 9.31
- 热变形温度 [℃]: 214.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 182 MPa | 26400 psi | ASTM D638 |
| Tensile Strength, Yield | 182 MPa | 26400 psi | ASTM D638 |
| Elongation at Break | 3.7 % | 3.7 % | ASTM D638 |
| Elongation at Yield | 3.7 % | 3.7 % | ASTM D638 |
| Tensile Modulus | 9.58 GPa | 1390 ksi | ASTM D638 |
| Flexural Strength | 290 MPa | 42100 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Thickness 3.18 mm | 2.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 12.4 J/cm @Thickness 3.18 mm | 23.2 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 14.1 kJ/m² | 6.71 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 78.3 kJ/m² | 37.3 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 14.0 J | 10.3 ft-lb | ASTM D3763 |
| Impact Test | 3.04 J | 2.24 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature 20.0 °C | 40.0 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |