- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 0.12
- 缺口冲击强度: 0.366
- 断裂伸长率 [%]: 89.6
- 弯曲强度 [MPa]: 31.4
- 弯曲模量 [MPa]: 2.76
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 - 1.44 g/cc | 0.0375 - 0.0520 lb/in³ | Average value: 1.24 g/cc Grade Count:15 |
| Filler Content | 15.0 - 40.0 % | 15.0 - 40.0 % | Average value: 25.6 % Grade Count:8 |
| Water Absorption | 0.120 - 0.300 % | 0.120 - 0.300 % | Average value: 0.192 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00394 cm/cm Grade Count:15 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.0160 cm/cm | 0.00200 - 0.0160 in/in | Average value: 0.00443 cm/cm Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 31.4 - 234 MPa | 4560 - 34000 psi | Average value: 150 MPa Grade Count:15 |
| Elongation at Break | 1.50 - 10.0 % | 1.50 - 10.0 % | Average value: 3.36 % Grade Count:12 |
| Modulus of Elasticity | 2.30 - 27.6 GPa | 333 - 4000 ksi | Average value: 13.0 GPa Grade Count:13 |
| Flexural Yield Strength | 89.6 - 372 MPa | 13000 - 54000 psi | Average value: 249 MPa Grade Count:13 |
| Flexural Modulus | 2.76 - 22.1 GPa | 400 - 3200 ksi | Average value: 12.5 GPa Grade Count:13 |
| Izod Impact, Notched | 0.366 - 1.60 J/cm | 0.685 - 3.00 ft-lb/in | Average value: 0.940 J/cm Grade Count:14 |
| Izod Impact, Unnotched | 3.79 - 10.7 J/cm | 7.10 - 20.0 ft-lb/in | Average value: 7.37 J/cm Grade Count:10 |
| Charpy Impact Unnotched | 6.00 - 6.00 J/cm² @Temperature -30.0 - -30.0 °C | 28.6 - 28.6 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 6.00 J/cm² Grade Count:1 |
| Charpy Impact, Notched | 1.00 - 1.00 J/cm² @Temperature -30.0 - -30.0 °C | 4.76 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.00 J/cm² Grade Count:1 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00 - 1.00e+14 ohm-cm | 5.00 - 1.00e+14 ohm-cm | Average value: 1.00e+13 ohm-cm Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 - 16.2 µm/m-°C | 8.00 - 9.00 µin/in-°F | Average value: 15.5 µm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 - 232 °C | 420 - 450 °F | Average value: 222 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 - 227 °C | 210 - 440 °F | Average value: 201 °C Grade Count:13 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:10 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 265 - 293 °C | 509 - 560 °F | Average value: 282 °C Grade Count:9 |
| Melt Temperature | 240 - 299 °C | 464 - 570 °F | Average value: 276 °C Grade Count:4 |
| Mold Temperature | 65.6 - 107 °C | 150 - 225 °F | Average value: 87.6 °C Grade Count:12 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 84.7 °C Grade Count:4 |
| Moisture Content | 0.170 - 1.20 % | 0.170 - 1.20 % | Average value: 0.523 % Grade Count:3 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 96.5 MPa Grade Count:9 |