- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 1.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc @Temperature 23.0 °C | 0.0452 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
| Filler Content | 23 % | 23 % | ISO 1172 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
| Spiral Flow | 450 cm | 177 in | AKRO | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 [mm/min]; ISO 527-1/2 | ||
| Elongation at Break | 4.5 % | 4.5 % | 5 [mm/min]; ISO 527-1/2 | ||
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1[mm/min]; ISO 527-1/2 | ||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1, DSC,10 [K/min] | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | HDT/A; ISO 75-1/2 | ||
| Deflection Temperature at 8.0 MPa | 115 °C | 239 °F | HDT/C; ISO 75-1/2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Nozzle Temperature | 240 - 295 °C | 464 - 563 °F | |||
| Zone 1 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 2 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 3 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 4 | 225 - 300 °C | 437 - 572 °F | |||
| Melt Temperature | 260 - 320 °C | 500 - 608 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 8 hour | 2 - 8 hour | |||
| Injection Pressure | 100 MPa | 14500 psi | |||
| Hold Pressure | 75.0 MPa | 10900 psi | |||
| Back Pressure | 0.400 - 1.00 MPa | 58.0 - 145 psi | |||
| Descriptive Properties | |||||
| Rate acc. FMVSS 302 (<100/min) | Passed | ||||
| Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||