- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.15 % | <= 0.15 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 200 MPa | 29000 psi | |||
| Elongation at Yield | 3.5 % | 3.5 % | |||
| 4.0 % | 4.0 % | flexural | |||
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | |||
| Flexural Strength | 290 MPa | 42100 psi | |||
| Flexural Modulus | 9.00 GPa | 1310 ksi | |||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | edgewise; ISO 179 1eU | ||
| 8.50 J/cm² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | |||
| Coefficient of Friction, Static | 0.25 | 0.25 | |||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | DIN 53752 | ||
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| 140 °C | 284 °F | short term | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 265 °C | 509 °F | mass temp | ||
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Zone 1 | 240 - 270 °C | 464 - 518 °F | |||
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |||
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |||
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec | 167 °F @Time 6.00 - 10.0 hour | Dehumidifying dryer | ||
| 105 °C @Time <=14400 sec | 221 °F @Time <=4.00 hour | or | |||
| Descriptive Properties | |||||
| Color | natural color (beige) | ||||