- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.18
- 缺口冲击强度: 1.6
- 断裂伸长率 [%]: 331
- 弯曲强度 [MPa]: 221.0
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm | 0.0010 - 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 221 MPa | 32100 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Flexural Yield Strength | 331 MPa | 48000 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 6.35 mm | 3.00 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00 - 50.0 ohm-cm | 5.00 - 50.0 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 °C | 8.00 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 559 °F | Stock |
| Mold Temperature | 82.0 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |