- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 0.38
- 拉伸强度 [MPa]: 86.0
- 弯曲模量 [MPa]: 3.85
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
| 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.44 GPa | 644 ksi | 1 mm/min; ISO 527 |
| 4.68 GPa | 679 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 128 MPa | 18600 psi | ISO 178 |
| 134 MPa | 19400 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.85 GPa | 558 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.88 GPa | 563 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.380 J/cm | 0.712 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.67 J/cm | 6.88 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 1.00 kJ/m² | 0.476 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C | 3.69 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.38 | 0.38 | ASTM D3702 Modified |
| K (wear) Factor | 10.1 x 10-8 mm³/N-M | 5.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 96.7 x 10-8 mm³/N-M | 48.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 56.4 µm/m-°C @Temperature -30.0 - 30.0 °C | 31.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 118 µm/m-°C @Temperature -30.0 - 30.0 °C | 65.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 218 °C @Thickness 3.20 mm | 424 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 196 °C @Thickness 3.20 mm | 385 °F @Thickness 0.126 in | unannealed; ASTM D648 | |