- 密度 [g/cm3]: 1.51
- 缺口冲击强度: 19.0
- 断裂伸长率 [%]: 265
- 弯曲模量 [MPa]: 10.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 180 MPa | 26100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.7 % | 3.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.9 GPa | 1580 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 265 MPa | 38400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.6 GPa | 1540 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 9.44 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 51.7 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |