- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.2
- 缺口冲击强度: 1.23
- 拉伸强度 [MPa]: 145.0
- 断裂伸长率 [%]: 214
- 弯曲模量 [MPa]: 7.58
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec | 0.20 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm | 0.0040 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm | 2.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.6 µm/m-°C | 22.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |