- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.7
- 缺口冲击强度: 9.08
- 拉伸强度 [MPa]: 75.8
- 断裂伸长率 [%]: 124
- 弯曲模量 [MPa]: 2.69
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % @Time 86400 sec | 0.70 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm @Thickness 3.17 mm | 0.020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm @Thickness 3.17 mm | 17.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 9.45 kV/mm | 240 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |