- 脆化温度 [℃]: -44.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.880 g/cc | 0.880 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 | 85 | ISO 868, 15 sec | ||
| Tensile Strength | 16.5 MPa | 2390 psi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Elongation at Break | 530 % | 530 % | 500 mm/min, measured parallel to flow; ISO 37 | ||
| 100% Modulus | 0.00920 GPa | 1.33 ksi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Tear Strength | 102 kN/m | 582 pli | Perpendicular to flow; ISO 34-B | ||
| 105 kN/m | 599 pli | Parallel to flow; ISO 34-B | |||
| Compression Set | 41 % @Temperature 23.0 °C, Time 259000 sec | 41 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 58 % @Temperature 70.0 °C, Time 86400 sec | 58 % @Temperature 158 °F, Time 24.0 hour | ISO 815 | |||
| Tensile Set | 85 % @Temperature 70.0 °C, Time 79200 sec | 85 % @Temperature 158 °F, Time 22.0 hour | VDA 675 217B | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 170 °C @Time 10800 sec | 338 °F @Time 3.00 hour | no distortion | ||
| Brittleness Temperature | -44.0 °C | -47.2 °F | ASTM D 746 | ||
| Flammability Test | 51 | 51 | mm/min; burn rate | ||
| Descriptive Properties | |||||
| Fogging, Gravimetric mg | DIN 75201B | ||||
| Fogging, Reflectance % | SAE J 1756 | ||||
| Odor Rating | 2 | SAE J1351 / FLTM BO131-01 (dry) | |||
| Ozone Resistance | 0 | 100 pphm / 200 hrs / 20% strain | |||