- 脆化温度 [℃]: -52.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | ISO 868, 15 sec | ||
| Tensile Strength | 10.7 MPa | 1550 psi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Elongation at Break | 590 % | 590 % | 500 mm/min, measured parallel to flow; ISO 37 | ||
| 100% Modulus | 0.00580 GPa | 0.841 ksi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Tear Strength | 51.0 kN/m | 291 pli | Perpendicular to flow; ISO 34-B | ||
| 75.0 kN/m | 428 pli | Parallel to flow; ISO 34-B | |||
| Compression Set | 44 % @Temperature 23.0 °C, Time 259000 sec | 44 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 51 % @Temperature 70.0 °C, Time 86400 sec | 51 % @Temperature 158 °F, Time 24.0 hour | ISO 815 | |||
| Tensile Set | 40 % @Temperature 70.0 °C, Time 79200 sec | 40 % @Temperature 158 °F, Time 22.0 hour | VDA 675 217B | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour | no distortion | ||
| Brittleness Temperature | -52.0 °C | -61.6 °F | ASTM D 746 | ||
| Flammability Test | 49 | 49 | mm/min; burn rate | ||
| Descriptive Properties | |||||
| Fogging, Reflectance % | SAE J 1756 | ||||
| Odor Rating | 2 | SAE J1351 / FLTM BO131-01 | |||
| Ozone Resistance | 0 | 100 pphm / 200 hrs / 20% strain | |||