| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ISO 2781 | ||
| Viscosity Measurement | 19 @Temperature 180 °C | 19 @Temperature 356 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | ISO 868 | ||
| Tensile Strength | 12.3 MPa | 1780 psi | ISO 37 | ||
| Elongation at Break | 490 % | 490 % | ISO 37 | ||
| 100% Modulus | 0.00400 GPa | 0.580 ksi | ISO 37 | ||
| Tear Strength | 35.0 kN/m | 200 pli | ISO 34-B | ||
| Compression Set | 18 % @Temperature 22.0 °C, Time 259000 sec | 18 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
| 24 % @Temperature 70.0 °C, Time 79200 sec | 24 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 39 % @Temperature 100 °C, Time 79200 sec | 39 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Descriptive Properties | |||||
| Bonds with | Polypropylene | ||||
| Polypropylene | |||||
| Polypropylene | |||||
| Chemical Resistance | Acetone | Good | |||
| Acids up to 80% | Excellent | ||||
| Alcohol | Excellent | ||||
| Alkalis | Excellent | ||||
| Brake fluid | Good | ||||
| Chlorinate solvents | Poor | ||||
| Diesel | Poor | ||||
| Ethylene glycol | Excellent | ||||
| Gasoline | Poor | ||||
| Salt solution | Excellent | ||||
| Soda lye | Excellent | ||||
| Water, 23°C | Excellent | ||||
| Water, 95°C | Excellent | ||||
| Transparency | Opaque | ||||