- 密度 [g/cm3]: 1.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 70 | 70 | DIN 53505/ISO 868 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Elongation at Break | 750 % | 750 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Compression Set | 10 % @Temperature 23.0 °C, Time 259000 sec | 10 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 45 % @Temperature 70.0 °C, Time 79200 sec | 45 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 65 % @Temperature -25.0 °C, Time 79200 sec | 65 % @Temperature -13.0 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | |||
| Descriptive Properties | |||||
| Color | Grey | ||||