- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 30 | 30 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 2.80 MPa | 406 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 420 % | 420 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 12.0 kN/m | 68.5 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 8.0 % @Temperature 23.0 °C, Time 259000 sec | 8.0 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 16 % @Temperature 70.0 °C, Time 79200 sec | 16 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 28 % @Temperature 100 °C, Time 79200 sec | 28 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| 58 % @Temperature 120 °C, Time 79200 sec | 58 % @Temperature 248 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 250 °C | 356 - 482 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||