- 密度 [g/cm3]: 1.05
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 6.00 MPa | 870 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 470 % | 470 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 15.0 kN/m | 85.6 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 13 % @Temperature 23.0 °C, Time 259000 sec | 13 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 35 % @Temperature 70.0 °C, Time 86400 sec | 35 % @Temperature 158 °F, Time 24.0 hour | ISO 815 | |||
| 38 % @Temperature 100 °C, Time 86400 sec | 38 % @Temperature 212 °F, Time 24.0 hour | ISO 815 | |||
| 47 % @Temperature 120 °C, Time 86400 sec | 47 % @Temperature 248 °F, Time 24.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | <= 140 °C | <= 284 °F | |||
| Descriptive Properties | |||||
| Color | Black | ||||