- 密度 [g/cm3]: 1.12
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 70 | 70 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 7.10 MPa | 1030 psi | DIN 53504 / ISO 37 | ||
| Elongation at Break | 650 % | 650 % | DIN 53504 / ISO 37 | ||
| Peel Strength | 0.500 kN/m | 2.85 pli | to PS; Renault test D41 1916 | ||
| 1.60 kN/m | 9.13 pli | to HIPS; Renault test D41 1916 | |||
| Graves Tear Strength | 26.0 kN/m | 148 pli | DIN ISO 34-1 Method B (b) | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 - 230 °C | 392 - 446 °F | adhesion to engineering thermoplastics | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 - 14400 sec | 140 - 176 °F @Time 2.00 - 4.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||