- 密度 [g/cm3]: 0.89
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 65 | 65 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 11.0 MPa | 1600 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 770 % | 770 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 21.0 kN/m | 120 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 25 % @Temperature 23.0 °C, Time 259000 sec | 25 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 45 % @Temperature 70.0 °C, Time 79200 sec | 45 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 55 % @Temperature 100 °C, Time 79200 sec | 55 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | with dynamic stress | ||
| 120 °C | 248 °F | static | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Descriptive Properties | |||||
| Color | Translucent | ||||