- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 | 40 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 2.60 MPa | 377 psi | DIN 53504 / ISO 37 | ||
| Elongation at Break | 778 % | 778 % | DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 10.8 kN/m | 61.6 pli | DIN ISO 34-1 Method B (b) | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 250 °C | 356 - 482 °F | adhesion to engineering thermoplastics | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C @Time 7200 sec | 140 - 176 °F @Time 2.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||