- 密度 [g/cm3]: 1.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 2781 | ||
| Deformation | 37 % @Temperature 700 °C, Time 79200 sec | 37 % @Temperature 1290 °F, Time 22.0 hour | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | ISO 868 | ||
| Tensile Strength | 5.30 MPa | 769 psi | ISO 37 | ||
| Elongation at Break | 600 % | 600 % | ISO 37 | ||
| 100% Modulus | 0.00190 GPa | 0.276 ksi | ISO 37 | ||
| 300% Modulus | 0.00260 GPa | 0.377 ksi | ISO 37 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | |||
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Nozzle Temperature | 185 °C | 365 °F | |||
| Zone 1 | 160 °C | 320 °F | |||
| Zone 2 | 170 °C | 338 °F | |||
| Zone 3 | 180 °C | 356 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Drying Temperature | 90.0 °C @Time 7200 sec | 194 °F @Time 2.00 hour | |||
| Back Pressure | 0.340 MPa | 49.3 psi | |||
| Screw Speed | 25 - 75 rpm | 25 - 75 rpm | |||
| Descriptive Properties | |||||
| Acid-Base Resistance | Excellent | ||||
| Alcohol Resistance | Excellent | ||||
| Compression Set | Good | ||||
| Injection Pressure | Medium | ||||
| Injection Speed | Medium-high | ||||
| Motor Oil Resistance | Medium | ||||
| Plasticizing Speed | High | ||||
| Solvent Resistance | Medium | ||||
| UV-Ozone Stability | Excellent | ||||