- 密度 [g/cm3]: 1.22
- 脆化温度 [℃]: -31.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85.0 | 85.0 | ASTM D2240 |
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ASTM D412 |
| Tensile Stress | 5.00 MPa @Strain 100 % | 725 psi @Strain 100 % | ASTM D412 |
| 14.0 MPa @Strain 300 % | 2030 psi @Strain 300 % | ASTM D412 | |
| Elongation at Break | 620 % | 620 % | ASTM D412 |
| Tear Strength | 83.1 kN/m | 474 pli | Die C; ASTM D412 |
| Taber Abrasion, mg/1000 Cycles | 23.0 | 23.0 | ASTM D1044 |
| Abrasion | 20.0 | 20.0 | mm3; DIN 53516 |
| Compression Set | 23.0 % @Temperature 22.8 °C, Time 79200 sec | 23.0 % @Temperature 73.0 °F, Time 22.0 hour | ASTM D3995B |
| 33.0 % @Temperature 70.0 °C, Time 259000 sec | 33.0 % @Temperature 158 °F, Time 72.0 hour | ASTM D3995B | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 110 °C | 230 °F | ASTM D1525 |
| Brittleness Temperature | -31.0 °C | -23.8 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 °C | 392 °F | Gate Temperature; Extrusion |
| 205 - 210 °C | 401 - 410 °F | Injection | |
| Rear Barrel Temperature | 180 °C | 356 °F | Injection |
| Middle Barrel Temperature | 195 °C | 383 °F | Injection |
| Front Barrel Temperature | 200 °C | 392 °F | Injection |
| Nozzle Temperature | 200 - 215 °C | 392 - 419 °F | Injection |
| Zone 1 | 180 °C | 356 °F | Extrusion |
| Zone 2 | 195 °C | 383 °F | Extrusion |
| Zone 3 | 200 °C | 392 °F | Extrusion |
| Die Temperature | 215 °C | 419 °F | Extrusion |
| Mold Temperature | 25.0 - 60.0 °C | 77.0 - 140 °F | Injection |
| Injection Velocity | >= 10.0 mm/sec | >= 0.394 in/sec | Injection |
| Drying Temperature | 85.0 °C | 185 °F | Injection |
| 85.0 °C | 185 °F | Extrusion | |
| Dry Time | 4.00 hour | 4.00 hour | Injection |
| 4.00 hour | 4.00 hour | Extrusion | |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection |
| Clamp Pressure | 40.0 - 70.3 MPa | 5800 - 10200 psi | Injection |
| Screw Speed | 60.0 - 200 rpm | 60.0 - 200 rpm | Injection |