- 密度 [g/cm3]: 1.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 | ||
| Melt Index of Compound | 45 g/10 min @Load 5.00 kg, Temperature 190 °C | 45 g/10 min @Load 11.0 lb, Temperature 374 °F | cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | ASTM D2240 | ||
| Hardness, Shore D | 21 | 21 | ASTM D2240 | ||
| Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 | ||
| Elongation at Break | 880 % | 880 % | DIN 53504 | ||
| 100% Modulus | 0.00340 GPa | 0.493 ksi | DIN 53504 | ||
| 300% Modulus | 0.00700 GPa | 1.02 ksi | DIN 53504 | ||
| Tear Strength | 45.1 kN/m | 257 pli | DIN 53515 | ||
| Abrasion | 35 | 35 | [mm3]; ISO 4649 | ||
| Compression Set | 34 % @Temperature 23.0 °C, Time 252000 sec | 34 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 | ||
| 48 % @Temperature 70.0 °C, Time 86400 sec | 48 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 175 °C | 347 °F | Injection | ||
| Front Barrel Temperature | 180 °C | 356 °F | Injection | ||
| Adapter Temperature | 180 °C | 356 °F | Injection | ||
| Die Temperature | 170 °C | 338 °F | Injection | ||
| Melt Temperature | 145 - 170 °C | 293 - 338 °F | |||
| Descriptive Properties | |||||
| TMA High | 165°C | ||||
| TMA Low | 120°C | ||||