- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D995 |
| Melt Index of Compound | 45 g/10 min @Load 21.6 kg, Temperature 215 °C | 45 g/10 min @Load 47.6 lb, Temperature 419 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 96 | 96 | ASTM D2240 |
| Hardness, Shore D | 54 | 54 | ASTM D2240 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | DIN 53504 |
| Elongation at Break | 590 % | 590 % | ASTM D412 |
| 100% Modulus | 0.0120 GPa | 1.74 ksi | DIN 53504 |
| 300% Modulus | 0.0260 GPa | 3.77 ksi | DIN 53504 |
| Rebound | 35 % | 35 % | Bayshore; ASTM D2632 |
| Tear Strength | 145 kN/m | 830 pli | ASTM D624 |
| Abrasion | 27 | 27 | [mm3]; ISO 4649 |
| Compression Set | 26 % @Temperature 23.0 °C, Time 252000 sec | 26 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 46 % @Temperature 70.0 °C, Time 86400 sec | 46 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 190 - 200 °C | 374 - 392 °F | Huntsman/TMA |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 200 - 215 °C | 392 - 419 °F | Extrusion |
| Nozzle Temperature | 200 - 215 °C | 392 - 419 °F | Extrusion |
| Adapter Temperature | 200 - 215 °C | 392 - 419 °F | Extrusion |
| Die Temperature | 200 - 215 °C | 392 - 419 °F | Extrusion |