- 密度 [g/cm3]: 1.2
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D995 | ||
| Melt Index of Compound | 28 g/10 min @Load 21.6 kg, Temperature 190 °C | 28 g/10 min @Load 47.6 lb, Temperature 374 °F | cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | ASTM D2240 | ||
| Hardness, Shore D | 35 | 35 | ASTM D2240 | ||
| Tensile Strength at Break | 49.0 MPa | 7110 psi | DIN 53504 | ||
| Elongation at Break | 680 % | 680 % | ASTM D412 | ||
| 100% Modulus | 0.00650 GPa | 0.943 ksi | DIN 53504 | ||
| 300% Modulus | 0.0161 GPa | 2.34 ksi | DIN 53504 | ||
| Rebound | 38 % | 38 % | Bayshore; ASTM D2632 | ||
| Tear Strength | 112 kN/m | 640 pli | ASTM D624 | ||
| Abrasion | 25 | 25 | [mm3]; ISO 4649 | ||
| Compression Set | 21 % @Temperature 23.0 °C, Time 252000 sec | 21 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 | ||
| 38 % @Temperature 70.0 °C, Time 86400 sec | 38 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 160 - 175 °C | 320 - 347 °F | Huntsman/TMA | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
| 25.0 - 45.0 °C | 77.0 - 113 °F | Injection | |||
| Front Barrel Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion | ||
| Nozzle Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion | ||
| 185 - 210 °C | 365 - 410 °F | Injection | |||
| Adapter Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion | ||
| Die Temperature | 180 - 205 °C | 356 - 401 °F | Extrusion | ||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | Injection | ||
| Descriptive Properties | |||||
| Heating Zone | 190-210°C | Injection | |||