Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry物性表参数

Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry

Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry 物性表: Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry物性表及特性介绍,Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry注塑参数详情,如需Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry下载, 可到相关下载区下载

密度 [g/cm3]: 1.14

Physical Properties	Metric	English	Comments

Density	1.14 g/cc	0.0412 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0080 cm/cm	0.0080 in/in	ASTM D955
Melt Index of Compound	150 g/10 min @Load 21.6 kg, Temperature 190 °C	150 g/10 min @Load 47.6 lb, Temperature 374 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	82	82	ASTM D2240
Hardness, Shore D	35	35	ASTM D2240
Tensile Strength at Break	25.0 MPa	3630 psi	DIN 53504
Elongation at Break	700 %	700 %	DIN 53504
100% Modulus	0.00350 GPa	0.508 ksi	DIN 53504
300% Modulus	0.00750 GPa	1.09 ksi	DIN 53504
Tear Strength	35.0 kN/m	200 pli	ISO 34-1
Abrasion	40	40	mm³; ISO 4549

Thermal Properties	Metric	English	Comments
Flammability, UL94	V-0	V-0	Non-Halogen FR

Processing Properties	Metric	English	Comments
Feed Temperature	25.0 - 40.0 °C	77.0 - 104 °F	Extrusion
Front Barrel Temperature	160 - 200 °C	320 - 392 °F	Extrusion
Nozzle Temperature	170 - 205 °C	338 - 401 °F	Extrusion
	200 - 210 °C	392 - 410 °F	Injection
Adapter Temperature	175 - 200 °C	347 - 392 °F	Extrusion
Die Temperature	175 - 205 °C	347 - 401 °F	Extrusion
Melt Temperature	190 - 205 °C	374 - 401 °F	Injection
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F	Injection

Descriptive Properties
Heating Zone	170-210°C		Injection

关键词:
供应
Huntsman IROGRAN® A 85 P 4854 Ether-Based TPU-For Cable Industry
TPU