- 弯曲强度 [MPa]: 4.83
- 脆化温度 [℃]: -53.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 91 | 91 | 2 mm, 15 sec; ISO 868 | ||
| 92 | 92 | Air at 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength at Break | 7.31 MPa | 1060 psi | Across Flow; ASTM D412 | ||
| 7.5277 MPa | 1091.8 psi | Air at 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength, Ultimate | 4.83 MPa | 700 psi | Across Flow; ASTM D412 | ||
| Tensile Stress | 4.80 MPa @Strain 100 % | 696 psi @Strain 100 % | Across Flow; ASTM D412 | ||
| Elongation at Break | 296.4 % | 296.4 % | Air at 302°F, 168 hr; ASTM D573 | ||
| 390 % | 390 % | Across Flow; ASTM D412 | |||
| Tear Strength | 31.0 kN/m | 177 pli | 73°F, Die C, Across Flow; ASTM D624 | ||
| Compression Set | 53 % | 53 % | 158°F, 22 hr; ASTM D395 | ||
| 62 % | 62 % | 212°F, 70 hr; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -53.9 °C | -65.0 °F | ASTM D746 | ||
| Flammability, UL94 | HB @Thickness 1.10 mm | HB @Thickness 0.0433 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Descriptive Properties | |||||
| Change in Mass in IRM 903 Oil at 257°F for 70 hr | 72 | ||||
| Color | Black | ||||
| Form | Pellets | ||||