- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 62 | 62 | 2 mm, 15 sec; ISO 868 | ||
| 67 | 67 | Air at 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength at Break | 4.50 MPa | 653 psi | Air at 302°F, 168 hr; ASTM D573 | ||
| 5.00 MPa | 725 psi | Across Flow; ASTM D412 | |||
| Tensile Stress | 2.10 MPa @Strain 100 % | 305 psi @Strain 100 % | Across Flow; ASTM D412 | ||
| Elongation at Break | 440 % | 440 % | Across Flow; ASTM D412 | ||
| 475.2 % | 475.2 % | Air at 302°F, 168 hr; ASTM D573 | |||
| Tear Strength | 36.1 kN/m | 206 pli | 73°F, Die C; ASTM D624 | ||
| Compression Set | 18 % | 18 % | 73°F, 22 hr; ASTM D395 | ||
| 39 % | 39 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.7 | 2.7 | 1.96 mm; ASTM D150 | ||
| Dielectric Strength | 25.6 kV/mm | 650 kV/in | 2.03 mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | |||
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Die Temperature | 204 °C | 400 °F | Extrusion | ||
| Melt Temperature | 177 - 204 °C | 350 - 400 °F | Extrusion | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Back Pressure | 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellets | ||||