- 弯曲强度 [MPa]: 2.69
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 64 | 64 | .12 in; ASTM D2240 | ||
| 69 | 69 | Air at 302°F, 168 hr; ASTM D573 | |||
| Tensile Strength at Break | 2.555 MPa | 370.5 psi | Air at 302°F, 168 hr; ASTM D573 | ||
| 6.62 MPa | 960 psi | Across Flow; ASTM D412 | |||
| Tensile Strength, Ultimate | 2.69 MPa | 390 psi | Across Flow; ASTM D412 | ||
| Elongation at Break | 437 % | 437 % | Air at 302°F, 168 hr; ASTM D573 | ||
| 460 % | 460 % | Across Flow; ASTM D412 | |||
| Tear Strength | 23.0 kN/m | 131 pli | 73°F, Die C; ASTM D624 | ||
| Compression Set | 19 % | 19 % | 73°F, 22 hr; ASTM D395 | ||
| 39 % | 39 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.4 | 2.4 | ASTM D150 | ||
| Dielectric Strength | 34.3 kV/mm | 870 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | |||
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Die Temperature | 204 °C | 400 °F | Extrusion | ||
| Melt Temperature | 177 - 204 °C | 350 - 400 °F | Extrusion | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Back Pressure | 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | ||
| Descriptive Properties | |||||
| Color | Natural Color | ||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.