- 密度 [g/cm3]: 0.95
- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 2781 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 90.0 | 90.0 | ISO 868 |
| Hardness, Shore D | 38.0 | 38.0 | ISO 868 |
| Tensile Strength at Break | 12.4 MPa | 1800 psi | ISO 37 |
| Tensile Stress | 7.31 MPa @Strain 100 % | 1060 psi @Strain 100 % | ISO 37 |
| 9.58 MPa @Strain 300 % | 1390 psi @Strain 300 % | ISO 37 | |
| Elongation at Break | 500 % | 500 % | ISO 37 |
| Tear Strength | 57.8 kN/m | 330 pli | ISO 34-1 |
| Compression Set | 49.0 % @Temperature 70.0 °C, Time 79200 sec | 49.0 % @Temperature 158 °F, Time 22.0 hour | ASTM D3995B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 205 °C | 401 °F | Gate Temperature; Extrusion |
| 200 - 230 °C | 392 - 446 °F | Injection | |
| Rear Barrel Temperature | 185 °C | 365 °F | Injection |
| Middle Barrel Temperature | 190 °C | 374 °F | Injection |
| Front Barrel Temperature | 195 °C | 383 °F | Injection |
| Nozzle Temperature | 195 - 225 °C | 383 - 437 °F | Injection |
| Zone 1 | 185 °C | 365 °F | Extrusion |
| Zone 2 | 195 °C | 383 °F | Extrusion |
| Zone 3 | 200 °C | 392 °F | Extrusion |
| Die Temperature | 210 °C @Pressure 4.80 - 17.0 MPa | 410 °F @Pressure 696 - 2470 psi | Extrusion |
| Mold Temperature | 10.0 - 50.0 °C | 50.0 - 122 °F | Injection |
| Injection Velocity | >= 50.0 mm/sec | >= 1.97 in/sec | Injection |
| Drying Temperature | 80.0 °C | 176 °F | Injection |
| 80.0 °C | 176 °F | Extrusion | |
| Dry Time | 3.00 hour | 3.00 hour | Injection |
| 3.00 hour | 3.00 hour | Extrusion | |
| Back Pressure | 0.400 - 0.800 MPa | 58.0 - 116 psi | Injection |
| Clamp Pressure | 40.0 - 70.3 MPa | 5800 - 10200 psi | Injection |
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | Injection |