- 脆化温度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ASTM D792 and ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 @Time 15.0 sec | 65 @Time 0.00417 hour | 2 mm; ISO 868 |
| Tensile Strength at Break | 4.70 MPa | 682 psi | Across Flow; ASTM D412 and ISO 37 |
| Tensile Stress | 2.10 MPa @Strain 100 % | 305 psi @Strain 100 % | Across Flow; ASTM D412 and ISO 37 |
| Elongation at Break | 420 % | 420 % | Across Flow; ASTM D412 and ISO 37 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |