| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 70 | 70 | ASTM D2240 | ||
| 60 @Treatment Temp. 140 °C, Time 3.629e+6 sec | 60 @Treatment Temp. 284 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| 67 @Treatment Temp. 120 °C, Time 3.629e+6 sec | 67 @Treatment Temp. 248 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| 75 @Treatment Temp. 100 °C, Time 3.60e+6 sec | 75 @Treatment Temp. 212 °F, Time 1000 hour | water immersion | |||
| Tensile Strength | 15.0 MPa | 2180 psi | ASTM D412 | ||
| 8.85 MPa @Treatment Temp. 140 °C, Time 3.629e+6 sec | 1280 psi @Treatment Temp. 284 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| 11.25 MPa @Treatment Temp. 100 °C, Time 3.60e+6 sec | 1632 psi @Treatment Temp. 212 °F, Time 1000 hour | water immersion | |||
| 12.15 MPa @Treatment Temp. 120 °C, Time 3.629e+6 sec | 1762 psi @Treatment Temp. 248 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| Elongation at Break | 600 % | 600 % | ASTM D412 | ||
| 378 % @Treatment Temp. 140 °C, Time 3.629e+6 sec | 378 % @Treatment Temp. 284 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| 480 % @Treatment Temp. 100 °C, Time 3.60e+6 sec | 480 % @Treatment Temp. 212 °F, Time 1000 hour | water immersion | |||
| 702 % @Treatment Temp. 120 °C, Time 3.629e+6 sec | 702 % @Treatment Temp. 248 °F, Time 1008 hour | heat aging; ASTM D573-99 | |||
| Compression Set | 20 % @Temperature 23.0 °C, Time 79200 sec | 20 % @Temperature 73.4 °F, Time 22.0 hour | ASTM D395 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 170 °C | 338 °F | extrusion | ||
| 180 °C | 356 °F | injection | |||
| Nozzle Temperature | 205 °C | 401 °F | |||
| Adapter Temperature | 190 °C | 374 °F | |||
| Die Temperature | 190 °C | 374 °F | |||
| Melt Temperature | 190 °C | 374 °F | extrusion | ||
| 205 °C | 401 °F | injection | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Back Pressure | 0.350 MPa | 50.8 psi | |||
| Descriptive Properties | |||||
| Injection Speed | fast | ||||