- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.21
- 断裂伸长率 [%]: 159
- 弯曲模量 [MPa]: 4.14
- 硬度: 127.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ASTM D 570(2) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 107 | 107 | ASTM D785 |
| Hardness, Rockwell R | 127 | 127 | ASTM D785 |
| Hardness, Shore D | 88 | 88 | ASTM D2240 |
| Tensile Strength | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | ASTM D638 |
| Flexural Yield Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Compressive Strength | 138 MPa | 20000 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 2.93 GPa | 425 ksi | ASTM D695 |
| Izod Impact, Notched | 0.21 J/cm | 0.40 ft-lb/in | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | Dry vs. Steel; QTM55007 |
| K (wear) Factor | 755 x 10-8 mm³/N-M | 375 x 10-10 in³-min/ft-lb-hr | QTM 55010 |
| Limiting Pressure Velocity | 0.298 MPa-m/sec | 8500 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | >= 1e+13 ohm | >= 1e+13 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | Short Term; ASTM D149 |
| Dissipation Factor | 0.003 @Frequency 1e+6 Hz | 0.003 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.8 µm/m-°C @Temperature -40.0 - 150 °C | 26.0 µin/in-°F @Temperature -40.0 - 302 °F | ASTM E831 |
| Thermal Conductivity | 0.252 W/m-K | 1.75 BTU-in/hr-ft²-°F | ASTM E1530-11 |
| Melting Point | 340 °C | 644 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 249 °C | 480 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/8 inch (Estimated Rating) |