- 吸水率 [%]: 0.001
- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 186.0
- 弯曲模量 [MPa]: 15.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.457 g/cc | 1.457 g/cc | ASTM D792 | ||
| Water Absorption | 0.0010 % | 0.0010 % | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 15.2 GPa | 2200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 265 MPa | 38500 psi | ASTM D790 | ||
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 10 - 100 ohm-cm | 10 - 100 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 299 °C | 570 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 399 - 427 °C | 750 - 800 °F | Molding | ||
| Mold Temperature | >= 149 °C | >= 300 °F | |||
| Drying Temperature | 149 °C | 300 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.