- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.53
- 断裂伸长率 [%]: 103
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 4.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm @Thickness 3.17 mm | 0.0060 - 0.0080 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 - 0.690 J/cm @Thickness 6.35 mm | 0.993 - 1.29 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 371 - 399 °C | 700 - 750 °F | Stock |
| Mold Temperature | 149 °C | 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |