- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0070 - 0.012 cm/cm | 0.0070 - 0.012 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 25 % | 25 % | ISO 527 | ||
| Flexural Strength | 165 MPa | 23900 psi | ISO 178 | ||
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ISO 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1000 Hz | 3.2 @Frequency 1000 Hz | ISO 60250 | ||
| Dissipation Factor | 0.0033 @Frequency 1000 Hz | 0.0033 @Frequency 1000 Hz | ISO 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | >= 340 °C | >= 644 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ISO75A | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |||
| Descriptive Properties | |||||
| Form | Pellets | ||||